基本性能 |
熔体流动速率 |
2.16kg at 220C |
ASTM D-1238 |
8.5 |
g/10min |
|
机械性能 |
泊松比 |
|
ASTM E-132 |
0.45 |
|
|
弯曲模量 |
-40C(-40F) |
ASTM D-790 IB |
172(25) |
MPa(kpsi) |
|
|
弯曲模量 |
100C(212F) |
ASTM D-790 IB |
28(4.1) |
MPa(kpsi) |
|
|
硬度 |
|
ASTM D-2240 |
40 |
|
|
|
IZOD冲击强度 |
23C(73F),6.35mm(0.25in) |
ASTM D-256-A |
NB |
J/m(ft lb/in) |
|
|
撕裂强度 |
|
ASTM D-1004 |
95(550) |
KN/m(lb/in) |
|
|
断裂伸长率 |
|
ASTM D-638 |
700 |
% |
|
|
拉伸应力 |
张力 10% |
ASTM D-638 |
3.5(0.5) |
MPa(kpsi) |
|
|
IZOD冲击强度 |
-40C(-40F),6.35mm(0.25in) |
ASTM D-256-A |
NB |
J/m(ft lb/in) |
|
|
拉伸应力 |
张力 5% |
ASTM D-638 |
2.4(0.4) |
MPa(kpsi) |
|
|
断裂抗拉强度 |
|
ASTM D-638 |
20(2.9) |
MPa(kpsi) |
|
|
弯曲模量 |
23C(73F) |
ASTM D-790 IB |
55(8.0) |
MPa(kpsi) |
|
|
|