物理性能 |
泰伯磨耗量 |
H 18轮 |
ASTM D-1044 |
80 |
mg/1000rev |
|
熔体流动速率 |
|
ASTM D-1238 |
8.5 |
g/10min |
|
|
比重 |
|
ASTM D-792 |
1.11 |
|
|
|
泰伯磨耗量 |
CS-17轮 |
ASTM D-1044 |
15 |
mg/1000rev |
|
|
机械性能 |
埃佐冲击强度 |
23℃ |
ASTM D-256 |
不破裂 |
J/m |
|
初耐撕裂性能 |
|
ASTM D-1004 |
95 |
kn/m |
|
|
拉伸力 |
5%伸长 |
|
ASTM D-638 |
2.4 |
Mpa |
|
10%伸长 |
|
ASTM D-638 |
3.5 |
Mpa |
|
|
断裂拉伸力 |
|
ASTM D-638 |
27.6 |
Mpa |
|
|
揉曲模量 |
23℃ |
ASTM D-790 |
55 |
Mpa |
|
|
硬度计硬度 |
|
ASTM D-2240 |
40 |
|
|
|
断裂伸长 |
|
ASTM D-638 |
600 |
% |
|
|
热性能 |
热畸变温度 |
@0.5Mpa |
ASTM D-648 |
55 |
℃ |
|
维卡软化点 |
|
ASTM D-1525 |
34 |
℃ |
|
|
熔点 |
|
ASTM D-3418 |
193 |
℃ |
|
|
热畸变温度 |
@0.18Mpa |
ASTM D-648 |
N/A |
℃ |
|
|
其它性能 |
耐揉曲切口增长性能 |
|
ASTM D-1052 |
>1×106 |
|