K树脂 PB-5925 台湾奇美实业股份有限公司
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | 23℃ | ASTM D-792 | 1.02 | --- |
| 浊度 | 1/8" | ASTM D-1003 | 2.5 | --- | |
| 光线透光率 | 1/8" | ASTM D-1003 | 88 | % | |
| 机械性能 | 硬度 | --- | --- | 72 | Shore D |
| 引张强度 | 1/8",6mm/min | ASTM D-638 | 350 | kg/cm2 | |
| 弯曲强度 | 1/4",2.8mm/min | ASTM D-790 | 440 | kg/cm2 | |
| 弯曲弹性率 | 1/4",2.8mm/min | ASTM D-790 | 18000 | kg/cm2 | |
| IZOD缺口冲击强度 | 1/4",23℃ | ASTM D-256 | 2.5 | kg.cm/cm | |
| 热 性 能 | 维卡软化点 | 1/8",50℃/hr | ASTM D-1525 | 92 | ℃ |
| 热变形温度 | 1/4",120℃/hr | ASTM D-648 | 74 | ℃ | |
| 其它性能 | 流动系数 | 200℃,5Kg | ASTM D-1238 | 11 | g/10min |