NORYL PPO MX6119物性表 Will be commercialized as IGN5531. 20% glass reinforced PPE+PS. Automotive ignitions systems: coil formers, insulators. Japanese translation material.   TYPICAL PROPERTIES (1) MECHA NICAL机械性能 Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min / 抗张程度,屈服,类型I,5 mm/min 88 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min / 抗张程度,断裂,类型I,5 mm/min 88 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min / 拉伸伸长,屈服,类型I,5 mm/min 2 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min / 拉伸伸长,断裂,类型I,5 mm/min 2 % ASTM D 638 Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min 6090 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 144 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距 5570 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C / 无缺口悬臂梁冲击 23°C 411 J/m ASTM D 4812 Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C 85 J/m ASTM D 256 Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C 1 J ASTM D 3763 THERMAL Value Unit Standard Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50 155 °C ASTM D 1525 HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火 155 °C ASTM D 648 HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火 148 °C ASTM D 648 CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动 3.42E-05 1/°C ASTM E 831 CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向 6.48E-05 1/°C ASTM E 831 PHYSICAL Value Unit Standard Specific Gravity/比重 1.21 - ASTM D 792 Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm 0.1 - 0.3 % SABIC Method Mold Shrinkage, xflow, 3.2 mm / 模塑收缩量，横向，3.2 mm 0.3 - 0.5 % SABIC Method Melt Flow Rate / 熔流率, 300°C/5.0 kgf 5.2 g/10 min ASTM D 1238