ABS L840 宁波乐金（LG）甬兴化工有限公司
超耐热
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.05 | --- |
| 模具收缩率 | --- | ASTM D-955 | 0.4-0.7 | % | |
| 熔体流动速率 | 220℃ 10kg | ASTM D-1238 | 7 | g/10min | |
| 机械性能 | 拉伸强度 | --- | ASTM D-638 | 470 | kg/cm2 |
| 伸长率 | --- | ASTM D-638 | 25 | % | |
| 弯曲强度 | --- | ASTM D-790 | 730 | kg/cm2 | |
| 弯曲模量 | --- | ASTM D-790 | 23200 | kg/cm2 | |
| 洛氏硬度 | --- | ASTM D-785 | 103 | R | |
| IZOD冲击强度 | 1/4〃带缺口 | ASTM D-256 | 19 | kg.cm/cm | |
| 热 性 能 | 热变形温度 | 18.5kg/cm2未退火 | ASTM D-648 | 103 | ℃ |
| 维卡软化点 | 1000g | ASTM D-1525 | 125 | ℃ |