ABS L849 宁波乐金（LG）甬兴化工有限公司
超高耐热
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.04 | --- |
| 模具收缩率 | --- | ASTM D-955 | 0.3-0.5 | % | |
| 熔体流动速率 | 220℃ 10kg | ASTM D-1238 | 2 | g/10min | |
| 机械性能 | 拉伸强度 | --- | ASTM D-638 | 480 | kg/cm2 |
| 伸长率 | --- | ASTM D-638 | 20 | % | |
| 弯曲强度 | --- | ASTM D-790 | 820 | kg/cm2 | |
| 弯曲模量 | --- | ASTM D-790 | 23000 | kg/cm2 | |
| IZOD冲击强度 | 1/4〃带缺口 | ASTM D-256 | 13 | kg.cm/cm | |
| 洛氏硬度 | --- | ASTM D-785 | 106 | R | |
| 热 性 能 | 热变形温度 | 18.5kg/cm2未退火 | ASTM D-648 | 115 | ℃ |
| 维卡软化点 | 1000g | ASTM D-1525 | 142 | ℃ |